Oxide-nitride-oxide stack having multiple oxynitride layers

ABSTRACT

An embodiment of a semiconductor memory device including a multi-layer charge storing layer and methods of forming the same are described. Generally, the device includes a channel formed from a semiconducting material overlying a surface on a substrate connecting a source and a drain of the memory device; a tunnel oxide layer overlying the channel; and a multi-layer charge storing layer including an oxygen-rich, first oxynitride layer on the tunnel oxide layer in which a stoichiometric composition of the first oxynitride layer results in it being substantially trap free, and an oxygen-lean, second oxynitride layer on the first oxynitride layer in which a stoichiometric composition of the second oxynitride layer results in it being trap dense. In one embodiment, the device comprises a non-planar transistor including a gate having multiple surfaces abutting the channel, and the gate comprises the tunnel oxide layer and the multi-layer charge storing layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of co-pending U.S. application Ser. No. 11/811,958, filed Jun. 13, 2007, which claims the benefit of priority under 35 U.S.C. 119(e) to U.S. Provisional Patent Application Ser. No. 60/931,947, filed May 25, 2007, both of which are incorporated by reference herein.

TECHNICAL FIELD

This invention relates to semiconductor processing and, more particularly to an oxide-nitride-oxide stack having an improved oxide-nitride or oxynitride layer and methods of forming the same.

BACKGROUND

Non-volatile semiconductor memories, such as a split gate flash memory, typically use a stacked floating gate type field effect transistors, in which electrons are induced into a floating gate of a memory cell to be programmed by biasing a control gate and grounding a body region of a substrate on which the memory cell is formed.

An oxide-nitride-oxide (ONO) stack is used as either a charge storing layer, as in silicon-oxide-nitride-oxide-silicon (SONOS) transistor, or as an isolation layer between the floating gate and control gate, as in a split gate flash memory.

FIG. 1 is a partial cross-sectional view of an intermediate structure for a semiconductor device 100, such as a memory device, having a SONOS gate stack or structure 102 including a conventional ONO stack 104 formed over a surface 106 of a silicon substrate 108 according to a conventional method. In addition, the device 100 typically further includes one or more diffusion regions 110, such as source and drain regions, aligned to the gate stack and separated by a channel region 112. Briefly, the SONOS structure 102 includes a poly-silicon (poly) gate layer 114 formed upon and in contact with the ONO stack 104. The poly gate layer 114 is separated or electrically isolated from the substrate 108 by the ONO stack 104. The ONO stack 104 generally includes a lower oxide layer 116, a nitride or oxynitride layer 118 which serves as a charge storing or memory layer for the device 100, and a top, high-temperature oxide (HTO) layer 120 overlying the nitride or oxynitride layer.

One problem with conventional SONOS structures 102 and methods of forming the same is the poor data retention of the nitride or oxynitride layer 118 that limits the device 100 lifetime and/or its use in several applications due to leakage current through the layer.

Another problem with conventional SONOS structures 102 and methods of forming the same is the stoichiometry of the oxynitride layer 118 is neither uniform nor optimized across the thickness of the layer. In particular, the oxynitride layer 118 is conventionally formed or deposited in a single step using a single process gas mixture and fixed or constant processing conditions in an attempt to provide a homogeneous layer having a high nitrogen and high oxygen concentration across the thickness of the relatively thick layer. However, due to top and bottom effects this results in nitrogen, oxygen and silicon concentrations, which can vary throughout the conventional oxynitride layer 118. The top effect is caused by the order in which process gases are shut off following deposition. In particular, the silicon containing process gas, such as silane, is typically shut off first resulting in a top portion of the oxynitride layer 118 that is high in oxygen and/or nitride and low in silicon. Similarly, the bottom effect is caused by the order in which process gases are introduced to initiate deposition. In particular, the deposition of the oxynitride layer 118 typically follows an annealing step, resulting in a peak or relatively high concentration of ammonia (NH₃) at the beginning of the deposition process and producing in a bottom portion of the oxynitride layer that is low in oxygen and silicon and high in nitrogen. The bottom effect is also due to surface nucleation phenomena in which that oxygen and silicon that is available in the initial process gas mixture preferentially reacts with silicon at the surface of the substrate and does not contribute to the formation of the oxynitride layer. Consequently, the charge storage characteristics, and in particular programming and erase speed and data retention of a memory device 100 made with the ONO stack 104, are adversely effected.

Accordingly, there is a need for a memory device having an ONO stack with an oxynitride layer as a memory layer that exhibits improved programming and erase speed and data retention. There is a further need for a method or process of forming an ONO stack having an oxynitride layer that exhibits improved oxynitride stoichiometry.

SUMMARY

A semiconductor memory device including a multi-layer charge storing layer and methods of forming the same are provided. Generally, the device includes a channel formed from a semiconducting material overlying a surface on a substrate connecting a source and a drain of the memory device; a tunnel oxide layer overlying the channel; and a multi-layer charge storing layer including an oxygen-rich, first oxynitride layer on the tunnel oxide layer in which a stoichiometric composition of the first oxynitride layer results in it being substantially trap free, and an oxygen-lean, second oxynitride layer on the first oxynitride layer in which a stoichiometric composition of the second oxynitride layer results in it being trap dense. In one embodiment, the device comprises a non-planar transistor including a gate having multiple surfaces abutting the channel, and the gate comprises the tunnel oxide layer and the multi-layer charge storing layer. Other embodiments are also disclosed.

BRIEF DESCRIPTION OF THE DRAWINGS

These and various other features and advantages of the present structure and method will be apparent upon reading of the following detailed description in conjunction with the accompanying drawings and the appended claims provided below, where:

FIG. 1 (prior art) is a block diagram illustrating a cross-sectional side view of an intermediate structure for a memory device for which a method having an oxide-nitride-oxide (ONO) stack formed according to conventional method;

FIG. 2 is a block diagram illustrating a cross-sectional side view of a portion of a semiconductor device having a silicon-oxide-oxynitride-oxide-silicon structure including a multi-layer charge storing layer according to an embodiment of the present disclosure;

FIG. 3 is flow chart of a method for forming an oxide-oxynitride-oxide structure including a multi-layer charge storing layer according to an embodiment of the present disclosure;

FIG. 4 is a graph showing an improvement in data retention for a memory device using a memory layer formed according to the present disclosure as compared to a memory device using a conventional memory layer;

FIG. 5 is flow chart of a method for forming an oxide-oxynitride-oxide structure including a multi-layer charge storing layer according to another embodiment of the present disclosure;

FIG. 6 is an energy band diagram of a programmed conventional memory device having an ONO structure;

FIGS. 7A and 7B are energy band diagrams of a memory device including a multi-layer charge storing layer according to an embodiment of the present disclosure prior to and following programming;

FIG. 8A illustrates a non-planar multigate device including a split charge-trapping region;

FIG. 8B illustrates a cross-sectional view of the non-planar multigate device of FIG. 8A;

FIGS. 9A and 9B illustrate a non-planar multigate device including a split charge-trapping region and a horizontal nanowire channel;

FIGS. 10A and 10B illustrate a non-planar multigate device including a split charge-trapping region and a vertical nanowire channel;

FIGS. 11A and 11B illustrate a gate first scheme for fabricating the non-planar multigate device of FIG. 10A; and

FIGS. 12A and 12B illustrate a gate last scheme for fabricating the non-planar multigate device of FIG. 10A.

DETAILED DESCRIPTION

The present invention is directed generally to a device comprising a silicon-oxide-oxynitride-oxide-silicon gate structure including a multi-layer charge storing layer and methods for making the same. The gate structure and method are particularly useful for forming a memory layer in a memory device, such as a memory transistor.

In the following description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the present disclosure. It will be evident, however, to one skilled in the art that the present structure and method may be practiced without these specific details. In other instances, well-known structures, and techniques are not shown in detail or are shown in block diagram form in order to avoid unnecessarily obscuring an understanding of this description.

Reference in the description to “one embodiment” or “an embodiment” means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment. The appearances of the phrase “in one embodiment” in various places in the specification do not necessarily all refer to the same embodiment. The term “to couple” as used herein may include both to directly connect and to indirectly connect through one or more intervening components.

Briefly, the method involves forming a multi-layer charge storing layer including multiple oxynitride layers, such as silicon oxynitride (Si₂N₂O) layers, having differing concentrations of Oxygen, Nitrogen and/or Silicon. The oxynitride layers are formed at higher temperatures than nitride or oxynitride layers in conventional ONO structures, and each of the layers are formed using differing process gases mixtures and/or at differing flow rates. Generally, the oxynitride layers include at least a top oxynitride layer and a bottom oxynitride layer. In certain embodiments, the stoichiometric compositions of the layers is tailored or selected such that the lower or bottom oxynitride has a high oxygen and silicon content, and the top oxynitride layer has high silicon and a high nitrogen concentration with a low oxygen concentration to produce an oxygen-lean, silicon-rich nitride or oxynitride. The silicon-rich and oxygen-rich bottom oxynitride layer reduces stored charge loss without compromising device speed or an initial (beginning of life) difference between program and erase voltages. The silicon-rich, oxygen-lean top oxynitride layer increases a difference between programming and erase voltages of memory devices, thereby improving device speed, increasing data retention, and extending the operating life of the device. In some embodiments, the silicon-rich, oxygen-lean top oxynitride layer can further include a concentration of carbon selected to increase the number of traps therein.

Optionally, the ratio of thicknesses between the top oxynitride layer and the bottom oxynitride layer can be selected to facilitate forming of the oxynitride layers over a tunneling or first oxide layer of a silicon-oxide-oxynitride-oxide-silicon gate structure following the forming of the first oxide layer using a dry or wet oxidation.

A silicon-oxide-oxynitride-oxide-silicon structure and methods for fabricating the same according to various embodiments of the present disclosure will now be described in greater detail with reference to FIGS. 2 through 4.

FIG. 2 is a block diagram illustrating a cross-sectional side view of a portion of a semiconductor memory device 200 having a silicon-oxide-oxynitride-oxide-silicon gate structure including a multi-layer charge storing layer according to one embodiment. Referring to FIG. 2, the memory device 200 includes a silicon-oxide-oxynitride-oxide-silicon gate structure or gate stack 202 including a multi-layer charge storing layer 204 formed over a surface 206 of silicon layer on a substrate or a silicon substrate 208. In addition, the device 200 further includes one or more diffusion regions 210, such as source and drain regions or structures, aligned to the gate stack 202 and separated by a channel region 212. Generally, the silicon-oxide-oxynitride-oxide-silicon gate structure includes a silicon containing gate layer, such as a poly-silicon or poly gate layer 214 formed upon and in contact with the multi-layer charge storing layer 204, and a portion of the silicon layer or substrate 208. The poly gate layer 214 is separated or electrically isolated from the substrate 208 by the multi-layer charge storing layer 204. The silicon-oxide-oxynitride-oxide-silicon structure includes a thin, lower oxide layer or tunneling oxide layer 216 that separates or electrically isolates the gate stack 202 from the channel region 212, a top or blocking oxide layer 218, and the multi-layer charge storing layer 204. As noted above and as shown in FIG. 2, the multi-layer charge storing layer 204 includes at least two oxynitride layers, including a top oxynitride layer 220A and a bottom oxynitride layer 220B.

The substrate 208 may include any known silicon-based semiconductor material including silicon, silicon-germanium, silicon-on-insulator, or silicon-on-sapphire substrate. Alternatively, the substrate 208 may include a silicon layer formed on a non-silicon-based semiconductor material, such as gallium-arsenide, germanium, gallium-nitride, or aluminum-phosphide. In certain embodiments, the substrate 208 is a doped or undoped silicon substrate.

The lower oxide layer or tunneling oxide layer 216 of the silicon-oxide-oxynitride-oxide-silicon structure generally includes a relatively thin layer of silicon dioxide (SiO₂) of from about 15 angstrom (Å) to about 22 Å, and in some embodiments about 18 Å. The tunneling oxide layer 216 can be formed or deposited by any suitable means including, for example, being thermally grown or deposited using chemical vapor deposition (CVD). Generally, the tunnel oxide layer is formed or grown using a thermal oxidation in oxygen ambient. In one embodiment, the process involves a dry oxidation method in which the substrate 208 is placed in a in a deposition or processing chamber, heated to a temperature from about 700° C. to about 850° C., and exposed to oxygen for a predetermined period of time selected based on a desired thickness of the finished tunneling oxide layer 216. In another embodiment, the tunnel oxide layer is grown in an ISSG (In-Situ Steam Generation) chamber with a radical oxidation using a reaction between oxygen (O₂) and hydrogen (H₂) on the substrate at temperatures of at least 1000° C. Exemplary process times are from about 10 to about 100 minutes. The oxidation can be performed at atmospheric or at low pressure.

As noted above, the multi-layer charge storing layer generally includes at least two oxynitride layers having differing compositions of silicon, oxygen and nitrogen, and can have an overall thickness of from about 70 Å to about 150 Å, and in certain embodiments about 100 Å. In one embodiment, the oxynitride layers are formed or deposited in a low pressure CVD process using a silicon source, such as silane (SiH₄), chlorosilane (SiH₃Cl), dichlorosilane or DCS (SiH₂Cl₂), tetrachlorosilane (SiCl₄) or Bis-TertiaryButylAmino Silane (BTBAS), a nitrogen source, such as nitrogen (N2), ammonia (NH₃), nitrogen trioxide (NO₃) or nitrous oxide (N₂O), and an oxygen-containing gas, such as oxygen (O₂) or N₂O. Alternatively, gases in which hydrogen has been replaced by deuterium can be used, including, for example, the substitution of deuterated-ammonia (ND₃) for NH₃. The substitution of deuterium for hydrogen advantageously passivates Si dangling bonds at the silicon-oxide interface, thereby increasing an NBTI (Negative Bias Temperature Instability) lifetime of the devices.

For example, the lower or bottom oxynitride layer 220B can be deposited over the tunneling oxide layer 216 by placing the substrate 208 in a deposition chamber and introducing a process gas including N₂O, NH₃ and DCS, while maintaining the chamber at a pressure of from about 5 millitorr (mT) to about 500 mT, and maintaining the substrate at a temperature of from about 700° C. to about 850° C. and in certain embodiments at least about 760° C., for a period of from about 2.5 minutes to about 20 minutes. In particular, the process gas can include a first gas mixture of N₂O and NH₃ mixed in a ratio of from about 8:1 to about 1:8 and a second gas mixture of DCS and NH₃ mixed in a ratio of from about 1:7 to about 7:1, and can be introduced at a flow rate of from about 5 to about 200 standard cubic centimeters per minute (sccm). It has been found that an oxynitride layer produced or deposited under these condition yields a silicon-rich, oxygen-rich, bottom oxynitride layer 220B, that decrease the charge loss rate after programming and after erase, which is manifested in a small voltage shift in the retention mode.

The top oxynitride layer 220A can be deposited over the bottom oxynitride layer 220B in a CVD process using a process gas including N₂O, NH₃ and DCS, at a chamber pressure of from about 5 mT to about 500 mT, and at a substrate temperature of from about 700° C. to about 850° C. and in certain embodiments at least about 760° C., for a period of from about 2.5 minutes to about 20 minutes. In particular, the process gas can include a first gas mixture of N2O and NH3 mixed in a ratio of from about 8:1 to about 1:8 and a second gas mixture of DCS and NH3 mixed in a ratio of from about 1:7 to about 7:1, and can be introduced at a flow rate of from about 5 to about 20 sccm. It has been found that an oxynitride layer produced or deposited under these condition yields a silicon-rich, nitrogen-rich, and oxygen-lean top oxynitride layer 220A, which improves the speed and increases of the initial difference between program and erase voltage without compromising a charge loss rate of memory devices made using an embodiment of the silicon-oxide-oxynitride-oxide-silicon structure, thereby extending the operating life of the device.

In some embodiments, the silicon-rich, nitrogen-rich, and oxygen-lean top oxynitride layer 220A can be deposited over the bottom oxynitride layer 220B in a CVD process using a process gas including BTBAS and ammonia (NH₃) mixed at a ratio of from about 7:1 to about 1:7 to further include a concentration of carbon selected to increase the number of traps therein. The selected concentration of carbon in the second oxynitride layer can include a carbon concentration of from about 5% to about 15%.

In certain embodiments, the top oxynitride layer 220A is deposited sequentially in the same tool used to form the bottom oxynitride layer 220B, substantially without breaking vacuum on the deposition chamber. In certain embodiments, the top oxynitride layer 220A is deposited substantially without altering the temperature to which the substrate 208 was heated during deposition of the bottom oxynitride layer 220B. In one embodiment, the top oxynitride layer 220A is deposited sequentially and immediately following the deposition of the bottom oxynitride layer 220B by decreasing the flow rate of the N₂O/NH₃ gas mixture relative to the DCS/NH₃ gas mixture to provide the desired ratio of the gas mixtures to yield the silicon-rich, nitrogen-rich, and oxygen-lean top oxynitride layer 220A.

In certain embodiments, another oxide or oxide layer (not shown in these figures) is formed after the formation of the gate stack 202 in a different area on the substrate 208 or in the device using a steam oxidation. In this embodiment, the top oxynitride layer 220A and top or blocking oxide layer 218 of the silicon-oxide-oxynitride-oxide-silicon structure are beneficially steam annealed during the steam oxidation process. In particular, steam annealing improves the quality of the top or blocking oxide layer 218 reducing the number of traps formed near a top surface of the blocking oxide layer and near a top surface of the underlying top oxynitride layer 220A, thereby reducing or substantially eliminating an electric field that could otherwise form across the blocking oxide layer, which could result in back streaming of charge carriers therethrough and adversely affecting data or charge retention in the charge storing layer.

A suitable thickness for the bottom oxynitride layer 220B has been found to be from about 10 Å to about 80 Å, and a ratio of thicknesses between the bottom layer and the top oxynitride layer has been found to be from about 1:6 to about 6:1, and in certain embodiments at least about 1:4.

The top or blocking oxide layer 218 of the silicon-oxide-oxynitride-oxide-silicon structure includes a relatively thick layer of SiO₂ of from about 30 Å to about 70 Å, and in certain embodiments about 45 Å. The top or blocking oxide layer 218 can be formed or deposited by any suitable means including, for example, being thermally grown or deposited using CVD. In one embodiment, the top or blocking oxide layer 218 is a high-temperature-oxide (HTO) deposited using CVD process. Generally, the deposition process involves exposing the substrate 208 to a silicon source, such as silane, chlorosilane, or dichlorosilane, and an oxygen-containing gas, such as O₂ or N₂O in a deposition chamber at a pressure of from about 50 mT to about 1000 mT, for a period of from about 10 minutes to about 120 minutes while maintaining the substrate at a temperature of from about 650° C. to about 850° C.

In certain embodiments, the top or blocking oxide layer 218 is deposited sequentially in the same tool used to form the oxynitride layers 220A, 220B. In certain embodiments, the oxynitride layers 220A, 220B, and the top or blocking oxide layer 218 are formed or deposited in the same tool used to grow the tunneling oxide layer 216. Suitable tools include, for example, an ONO AVP, commercially available from AVIZA technology of Scotts Valley, Calif.

A method or forming or fabricating a silicon-oxide-oxynitride-oxide-silicon stack according to one embodiment will now be described with reference to the flowchart of FIG. 3.

Referring to FIG. 3, the method begins with forming a first oxide layer, such as a tunneling oxide layer 216, of the silicon-oxide-oxynitride-oxide-silicon gate stack 202 over a silicon containing layer on a surface of a substrate 208 (300). Next, the first or bottom oxynitride layer 220B of a multi-layer charge storing layer 204 including oxynitride is formed on a surface of the first oxide layer (302). As noted above, this first or bottom oxynitride layer 220B can be formed or deposited by a CVD process using a process gas including N₂O/NH₃ and DCS/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer. The second or top oxynitride layer 220A of the multi-layer charge storing layer 204 is then formed on a surface of the first or bottom oxynitride layer 220B (304). The second or top oxynitride layer 220A has a stoichiometric composition of oxygen, nitrogen and/or silicon different from that of the first or bottom oxynitride layer 220B. In particular, and as noted above, the second or top oxynitride layer 220A can be formed or deposited by a CVD process using a process gas including DCS/NH₃ and N₂O/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich, oxygen-lean top oxynitride layer. Finally, a top or blocking oxide layer 218 of the silicon-oxide-oxynitride-oxide-silicon structure is formed on a surface of the second layer of the multi-layer charge storing layer (306). As noted above, this top or blocking oxide layer 218 can be formed or deposited by any suitable means, but in some embodiments is deposited in a CVD process. In one embodiment the top or blocking oxide layer 218 is a high temperature oxide deposited in a HTO CVD process. Alternatively, the top or blocking oxide layer 218 can be thermally grown, however it will be appreciated that in this embodiment the thickness of the top oxynitride 220A may be adjusted or increased as some of the top oxynitride will be effectively consumed or oxidized during the process of thermally growing the top or blocking oxide layer 218.

Optionally, the method may further include forming or depositing a silicon containing layer on a surface of the top or blocking oxide layer 218 to form a silicon-oxide-oxynitride-oxide-silicon stack or structure (308). The silicon containing layer can be, for example, a polysilicon layer deposited by a CVD process to form a control or poly gate layer 214 of the transistor or device 200.

A comparison of data retention for a memory device using a memory layer formed according to an embodiment of the present disclosure as compared to a memory device using a conventional memory layer will now be made with reference to FIG. 4. In particular, FIG. 4 illustrates the change in threshold voltage of devices in an electronically erasable programmable read-only memory (EEPROM) during programming (VTP) during erase (VTE) over device life for an EEPROM made using a conventional ONO structure and a silicon-oxide-oxynitride-oxide-silicon structure having a multi-layer oxynitride layer. In gathering data for this figure both devices were pre-cycled for 100K cycles at an ambient temperature of 85° C.

Referring to FIG. 4, the graph or line 402 illustrates the change over time of a VTP for an EEPROM made using a conventional ONO structure having a single oxynitride layer without refreshing the memory after the initial writing—program or erase. Actual data points on line 402 are shown by unfilled circles, the remainder of the line showing an extrapolation of VTP to a specified end-of-life (EOL) for the EEPROM. Graph or line 404 illustrates the change over time of a VTE for the EEPROM made using a conventional ONO structure. Actual data points on line 404 are shown by filled circles, and the remainder of the line shows an extrapolation of VTE to EOL for the EEPROM. Generally, the specified difference between the VTE and VTP for an EEPROM at EOL is at least 0.5 V to be able to identify or sense the difference between the program and erase state. As seen from this figure an EEPROM made using a conventional ONO structure has a difference between VTE and VTP of about 0.35V at a specified EOL of 20 years. Thus, an EEPROM made using a conventional ONO structure and operated under the conditions described above will fail to meet the specified operating life by at least about 17 years.

In contrast, the change in VTP and VTE over time for an EEPROM made using a silicon-oxide-oxynitride-oxide-silicon structure having a multi-layer oxynitride layer, illustrated by lines 406 and 408 respectively, shows a difference between VTE and VTP of at least about 1.96V at the specified EOL. Thus, an EEPROM made using a silicon-oxide-oxynitride-oxide-silicon structure according to an embodiment of the present disclosure will meet and exceed the specified operating life of 20 years. In particular, graph or line 406 illustrates the change over time of VTP for an EEPROM using a silicon-oxide-oxynitride-oxide-silicon structure according to an embodiment of the present disclosure. Actual data points on line 406 are shown by unfilled squares, the remainder of the line showing an extrapolation of VTP to the specified EOL. Graph or line 408 illustrates the change over time of VTE for the EEPROM, and actual data points on line 408 are shown by filled squares, the remainder of the line showing an extrapolation of VTE to EOL.

A method or forming or fabricating a semiconductor device according to another embodiment is now described with reference to the flowchart of FIG. 5.

Referring to FIG. 5, the method begins with forming a tunneling oxide layer 216 on a substrate (500). Next, an oxygen-rich, first or bottom oxynitride layer 220B of a multi-layer charge storing layer 204 is formed on a surface of the tunneling oxide layer 216 (502). As noted above, this oxygen-rich, first or bottom oxynitride layer 220B can be formed or deposited by a CVD process using a process gas comprising a dichlorosilane (SiH₂Cl₂)/ammonia (NH₃) mixture at a ratio in the range of about 5:1 to 15:1; and a nitrous oxide (N₂O)/NH₃ mixture at a ratio in the range of about 2:1 to 4:1 and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer which is substantially trap free. That is the stoichiometric composition of the first or bottom oxynitride layer 220B comprises a high concentration of oxygen selected to increase retention performance of the multi-layer charge storing layer by acting as a barrier between charge trapped in the second or top oxynitride layer 220A and the substrate 208. The selected concentration of oxygen in the first or bottom oxynitride layer 220B can include an oxygen concentration of from about 15% to about 40%, and, in certain embodiments about 35%.

An oxygen-lean, second or top oxynitride layer 220A is then formed on a surface of the first or bottom oxynitride layer 220B (504). The second or top oxynitride layer 220A has a stoichiometric composition of oxygen, nitrogen and/or silicon different from that of the first layer. In particular, and as noted above, the second or top oxynitride layer 220A can be formed or deposited by a CVD process using a process gas using a process gas comprising a N₂O/NH₃ mixture at a ratio in the range of about 1:6 to 1:8 and a SiH₂Cl₂/NH₃ mixture at a ratio in the range of about 1.5:1 to 3:1 to provide a trap dense oxynitride layer having an oxygen concentration of about 5% or less. Thus, the second or top oxynitride layer 220A comprises a charge trap density at least 1000 times greater than the first or bottom oxynitride layer 220B.

Finally, a top or blocking oxide layer 218 is formed over the second or top oxynitride layer 220A of the multi-layer charge storing layer 204 (506). As noted above, this top or blocking oxide layer 218 can be formed or deposited by any suitable means. In one embodiment the second or blocking oxide layer 218 is formed a manner that results in thinning of the second or top oxynitride layer 220A to a predetermined thickness through oxidization of a portion of the second oxynitride layer. Finally, as noted above with respect to FIG. 4, the increased retention performance of the multi-layer charge storing layer 204 increases an end-of-life (EOL) for the semiconductor device at a specified difference between program voltage (VTP) and erase voltage (VTE) to at least about 20 years.

In another aspect, the multi-layer charge storing layer of the present disclosure has bandgap energy engineered to generate an electrical field opposing that built-up due to charge storage in the charge storing layer in a programmed state, thereby increasing data retention, without impacting programming voltages and/or device speed. An energy band diagram of a programmed conventional device including a channel in silicon substrate 602, a tunneling oxide layer 604, a homogeneous nitride or oxynitride charge storing layer 606, oxide blocking layer 608 and a polysilicon control gate 610 is illustrated in FIG. 6. Referring to FIG. 6, it is noted that large number of trapped charges located near the center of the charge storing layer 606 results in a build-up of a large electric field away from the tunneling oxide layer 604 towards the trapped charges, and which can cause or result in loss of stored charges

In contrast, in a memory device including the multi-layer charge storing layer of the present disclosure engineering the bandgap energy multi-layer charge storing layer results in a build-up of an electrical field pointing inward (from the charge storing layer toward the tunnel oxide), which opposes the build-up of the electric field due to the stored charge increasing charge retention. An unprogrammed memory device including a multi-layer charge storing layer 706 is shown in FIG. 7A. The device includes a channel in silicon substrate 702, a tunneling oxide layer 704, an oxygen-lean oxynitride layer 706A, an oxygen-rich bottom oxynitride layer 706B, an oxide blocking layer 708 and a polysilicon control gate 710. Referring to FIG. 7A, the trap sites in the oxygen-lean top oxynitride layer 706A, produces an electric field that will oppose the electric field produced by the trapped charges in the programmed device. The resultant bandgap diagram of a device including a multi-layer charge storing layer 706 in a programmed state is shown in FIG. 7A.

Implementations and Alternatives

In another aspect the present disclosure is directed to multigate or multigate-surface memory devices including charge-trapping regions overlying two or more sides of a channel formed on or above a surface of a substrate, and methods of fabricating the same. Multigate devices include both planar and non-planar devices. A planar multigate device (not shown) generally includes a double-gate planar device in which a number of first layers are deposited to form a first gate below a subsequently formed channel, and a number of second layers are deposited thereover to form a second gate. A non-planar multigate device generally includes a horizontal or vertical channel formed on or above a surface of a substrate and surrounded on three or more sides by a gate.

FIG. 8A illustrates one embodiment of a non-planar multigate memory device including a charge-trapping region. Referring to FIG. 8A, the memory device 800, commonly referred to as a finFET, includes a channel 802 formed from a thin film or layer of semiconducting material overlying a surface 804 on a substrate 806 connecting a source 808 and a drain 810 of the memory device. The channel 802 is enclosed on three sides by a fin which forms a gate 812 of the device. The thickness of the gate 812 (measured in the direction from source to drain) determines the effective channel length of the device.

In accordance with the present disclosure, the non-planar multigate memory device 800 of FIG. 8A can include a split charge-trapping region. FIG. 8B is a cross-sectional view of a portion of the non-planar memory device of FIG. 8A including a portion of the substrate 806, channel 802 and the gate 812 illustrating a multi-layer charge storing layer 814. The gate 812 further includes a tunnel oxide layer 816 overlying a raised channel 802, a blocking dielectric 818 and a metal gate layer 820 overlying the blocking layer to form a control gate of the memory device 800. In some embodiments a doped polysilicon may be deposited instead of metal to provide a polysilicon gate layer. The channel 802 and gate 812 can be formed directly on substrate 806 or on an insulating or dielectric layer 822, such as a buried oxide layer, formed on or over the substrate.

Referring to FIG. 8B, the multi-layer charge storing layer 814 includes at least one lower or bottom charge-trapping layer 824 including nitride closer to the tunnel oxide layer 816, and an upper or top charge-trapping layer 826 overlying the bottom charge-trapping layer. Generally, the top charge-trapping layer 826 includes a silicon-rich, oxygen-lean nitride layer and includes a majority of a charge traps distributed in multiple charge-trapping layers, while the bottom charge-trapping layer 824 includes an oxygen-rich nitride or silicon oxynitride, and is oxygen-rich relative to the top charge-trapping layer to reduce the number of charge traps therein. By oxygen-rich it is meant wherein a concentration of oxygen in the bottom charge-trapping layer 824 is from about 15 to about 40%, whereas a concentration of oxygen in top charge-trapping layer 826 is less than about 5%.

In one embodiment, the blocking dielectric 818 also includes an oxide, such as an HTO, to provide an ONNO structure. The channel 802 and the overlying ONNO structure can be formed directly on a silicon substrate 806 and overlaid with a doped polysilicon gate layer 820 to provide a SONNOS structure.

In some embodiments, such as that shown in FIG. 8B, the multi-layer charge storing layer 814 further includes at least one thin, intermediate or anti-tunneling layer 828 including a dielectric, such as an oxide, separating the top charge-trapping layer 826 from the bottom charge-trapping layer 824. The anti-tunneling layer 828 substantially reduces the probability of electron charge that accumulates at the boundaries of the upper nitride layer 826 during programming from tunneling into the bottom nitride layer 824, resulting in lower leakage current than for the structures illustrated in FIG. 1 and FIG. 6.

As with the embodiments described above, either or both of the bottom charge-trapping layer 824 and the top charge-trapping layer 826 can include silicon nitride or silicon oxynitride, and can be formed, for example, by a CVD process including N₂O/NH₃ and DCS/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer. The second nitride layer of the multi-layer charge storing structure is then formed on the middle oxide layer. The top charge-trapping layer 826 has a stoichiometric composition of oxygen, nitrogen and/or silicon different from that of the bottom charge-trapping layer 824, and may also be formed or deposited by a CVD process using a process gas including DCS/NH₃ and N₂O/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich, oxygen-lean top nitride layer.

In those embodiments including an intermediate or anti-tunneling layer 828 including oxide, the anti-tunneling layer can be formed by oxidation of the bottom oxynitride layer, to a chosen depth using radical oxidation. Radical oxidation may be performed, for example, at a temperature of 1000-1100° C. using a single wafer tool, or 800-900° C. using a batch reactor tool. A mixture of H₂ and O₂ gasses may be employed at a pressure of 300-500 Tor for a batch process, or 10-15 Tor using a single vapor tool, for a time of 1-2 minutes using a single wafer tool, or 30 min-1 hour using a batch process.

Finally, in those embodiments including a blocking dielectric 818 including oxide the oxide may be formed or deposited by any suitable means. In one embodiment the oxide of the blocking dielectric 818 is a high temperature oxide deposited in a HTO CVD process. Alternatively, the blocking dielectric 818 or blocking oxide layer may be thermally grown, however it will be appreciated that in this embodiment the top nitride thickness may be adjusted or increased as some of the top nitride will be effectively consumed or oxidized during the process of thermally growing the blocking oxide layer. A third option is to oxidize the top nitride layer to a chosen depth using radical oxidation.

A suitable thickness for the bottom charge-trapping layer 824 may be from about 30 Å to about 80 Å (with some variance permitted, for example ±10 A), of which about 5-20 Å may be consumed by radical oxidation to form the anti-tunneling layer 828. A suitable thickness for the top charge-trapping layer 826 may be at least 30 Å. In certain embodiments, the top charge-trapping layer 826 may be formed up to 130 Å thick, of which 30-70 Å may be consumed by radical oxidation to form the blocking dielectric 818. A ratio of thicknesses between the bottom charge-trapping layer 824 and top charge-trapping layer 826 is approximately 1:1 in some embodiments, although other ratios are also possible.

In other embodiments, either or both of the top charge-trapping layer 826 and the blocking dielectric 818 may include a high K dielectric. Suitable high K dielectrics include hafnium based materials such as HfSiON, HfSiO or HfO, Zirconium based material such as ZrSiON, ZrSiO or ZrO, and Yttrium based material such as Y₂O₃.

In another embodiment, shown in FIGS. 9A and 9B, the memory device can include a nanowire channel formed from a thin film of semiconducting material overlying a surface on a substrate connecting a source and a drain of the memory device. By nanowire channel it is meant a conducting channel formed in a thin strip of crystalline silicon material, having a maximum cross-sectional dimension of about 10 nanometers (nm) or less, and more preferably less than about 6 nm. Optionally, the channel can be formed to have <100> surface crystalline orientation relative to a long axis of the channel.

Referring to FIG. 9A, the memory device 900 includes a horizontal nanowire channel 902 formed from a thin film or layer of semiconducting material on or overlying a surface on a substrate 906, and connecting a source 908 and a drain 910 of the memory device. In the embodiment shown, the device has a gate-all-around (GAA) structure in which the nanowire channel 902 is enclosed on all sides by a gate 912 of the device. The thickness of the gate 912 (measured in the direction from source to drain) determines the effective channel length of the device.

In accordance with the present disclosure, the non-planar multigate memory device 900 of FIG. 9A can include a split charge-trapping region. FIG. 9B is a cross-sectional view of a portion of the non-planar memory device of FIG. 9A including a portion of the substrate 906, nanowire channel 902 and the gate 912 illustrating a split charge-trapping region. Referring to FIG. 9B, the gate 912 includes a tunnel oxide layer 914 overlying the nanowire channel 902, a split charge-trapping region, a blocking dielectric 916 and a gate layer 918 overlying the blocking layer to form a control gate of the memory device 900. The gate layer 918 can include a metal or a doped polysilicon. The multi-layer charge storing layer includes at least one inner charge-trapping layer 920 including nitride closer to the tunnel oxide layer 914, and an outer charge-trapping layer 922 overlying the inner charge-trapping layer. Generally, the outer charge-trapping layer 922 includes a silicon-rich, oxygen-lean nitride layer and includes a majority of a charge traps distributed in multiple charge-trapping layers, while the inner charge-trapping layer 920 includes an oxygen-rich nitride or silicon oxynitride, and is oxygen-rich relative to the outer charge-trapping layer to reduce the number of charge traps therein.

In some embodiments, such as that shown, the multi-layer charge storing layer further includes at least one thin, intermediate or anti-tunneling layer 924 including a dielectric, such as an oxide, separating outer charge-trapping layer 922 from the inner charge-trapping layer 920. The anti-tunneling layer 924 substantially reduces the probability of electron charge that accumulates at the boundaries of outer charge-trapping layer 922 during programming from tunneling into the inner charge-trapping layer 920, resulting in lower leakage current.

As with the embodiment described above, either or both of the inner charge-trapping layer 920 and the outer charge-trapping layer 922 can include silicon nitride or silicon oxynitride, and can be formed, for example, by a CVD process including N₂O/NH₃ and DCS/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer. The second nitride layer of the multi-layer charge storing structure is then formed on the middle oxide layer. The outer charge-trapping layer 922 has a stoichiometric composition of oxygen, nitrogen and/or silicon different from that of the inner charge-trapping layer 920, and may also be formed or deposited by a CVD process using a process gas including DCS/NH₃ and N₂O/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich, oxygen-lean top nitride layer.

In those embodiments including an intermediate or anti-tunneling layer 924 including oxide, the anti-tunneling layer can be formed by oxidation of the inner charge-trapping layer 920, to a chosen depth using radical oxidation. Radical oxidation may be performed, for example, at a temperature of 1000-1100° C. using a single wafer tool, or 800-900° C. using a batch reactor tool. A mixture of H₂ and O₂ gasses may be employed at a pressure of 300-500 Tor for a batch process, or 10-15 Tor using a single vapor tool, for a time of 1-2 minutes using a single wafer tool, or 30 min-1 hour using a batch process.

Finally, in those embodiments in which the blocking dielectric 916 includes oxide, the oxide may be formed or deposited by any suitable means. In one embodiment the oxide of blocking dielectric 916 is a high temperature oxide deposited in a HTO CVD process. Alternatively, the blocking dielectric 916 or blocking oxide layer may be thermally grown, however it will be appreciated that in this embodiment the thickness of the outer charge-trapping layer 922 may need to be adjusted or increased as some of the top nitride will be effectively consumed or oxidized during the process of thermally growing the blocking oxide layer.

A suitable thickness for the inner charge-trapping layer 920 may be from about 30 Å to about 80 Å (with some variance permitted, for example ±10 A), of which about 5-20 Å may be consumed by radical oxidation to form the anti-tunneling layer 924. A suitable thickness for the outer charge-trapping layer 922 may be at least 30 Å. In certain embodiments, the outer charge-trapping layer 922 may be formed up to 120 Å thick, of which 30-70 Å may be consumed by radical oxidation to form the blocking dielectric 916. A ratio of thicknesses between the inner charge-trapping layer 920 and the outer charge-trapping layer 922 is approximately 1:1 in some embodiments, although other ratios are also possible.

In other embodiments, either or both of the outer charge-trapping layer 922 and the blocking dielectric 916 may include a high K dielectric. Suitable high K dielectrics include hafnium based materials such as HfSiON, HfSiO or HfO, Zirconium based material such as ZrSiON, ZrSiO or ZrO, and Yttrium based material such as Y₂O₃.

In another embodiment, the memory device is or includes a non-planar device including a vertical nanowire channel formed in or from a semiconducting material projecting above or from a number of conducting, semiconducting layers on a substrate. In one version of this embodiment, shown in cut-away in FIG. 10A, the memory device 1000 includes a vertical nanowire channel 1002 formed in a cylinder of semiconducting material connecting a source 1004 and drain 1006 of the device. The channel 1002 is surrounded by a tunnel oxide layer 1008, a multi-layer charge storing layer 1110, a blocking layer 1012 and a gate layer 1014 overlying the blocking layer to form a control gate of the memory device 1000. The channel 1002 can include an annular region in an outer layer of a substantially solid cylinder of semiconducting material, or can include an annular layer formed over a cylinder of dielectric filler material. As with the horizontal nanowires described above, the channel 1002 can include polysilicon or recrystallized polysilicon to form a monocrystalline channel. Optionally, where the channel 1002 includes a crystalline silicon, the channel can be formed to have <100> surface crystalline orientation relative to a long axis of the channel.

In some embodiments, such as that shown in FIG. 10B, the multi-layer charge storing layer 1010 can be a multi-layer charge storing layer including at least a first or inner charge trapping layer 1016 closest to the tunnel oxide layer 1008, and a second or outer charge trapping layer 1018. Optionally, the first and second charge trapping layers can be separated by an intermediate oxide or anti-tunneling layer 1020.

As with the embodiments described above, either or both of the first charge trapping layer 1016 and the second charge trapping layer 1018 can include silicon nitride or silicon oxynitride, and can be formed, for example, by a CVD process including N₂O/NH₃ and DCS/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer.

Finally, either or both of the second charge trapping layer 1018 and the blocking layer 1012 may include a high K dielectric, such as HfSiON, HfSiO, HfO, ZrSiON, ZrSiO, ZrO, or Y₂O₃.

A suitable thickness for the first charge trapping layer 1016 may be from about 30 Å to about 80 Å (with some variance permitted, for example ±10 A), of which about 5-20 Å may be consumed by radical oxidation to form the anti-tunneling layer 1020. A suitable thickness for the second charge trapping layer 1018 may be at least 30 Å, and a suitable thickness for the blocking dielectric 1012 may be from about 30-70 Å.

The memory device 1000 of FIG. 10A can be made using either a gate first or a gate last scheme. FIG. 11A-F illustrate a gate first scheme for fabricating the non-planar multigate device of FIG. 10A. FIG. 12A-F illustrate a gate last scheme for fabricating the non-planar multigate device of FIG. 10A.

Referring to FIG. 11A, in a gate first scheme a first or lower dielectric layer 1102, such as a blocking oxide, is formed over a first, doped diffusion region 1104, such as a source or a drain, in a substrate 1106. A gate layer 1108 is deposited over the first dielectric layer 1102 to form a control gate of the device, and a second or upper dielectric layer 1110 formed thereover. As with embodiments described above, the first and second dielectric layers 1102, 1110, can be deposited by CVD, radical oxidation or be formed by oxidation of a portion of the underlying layer or substrate. The gate layer 1108 can include a metal deposited or a doped polysilicon deposited by CVD. Generally the thickness of the gate layer 1108 is from about 40-50 Å, and the first and second dielectric layers 1102, 1110, from about 20-80 Å.

Referring to FIG. 11B, a first opening 1112 is etched through the overlying gate layer 1108, and the first and second dielectric layers 1102, 1110, to the diffusion region 1104 in the substrate 1106. Next, layers including a tunnel oxide layer 1114, multi-layer charge storing layer 1116, and blocking dielectric 1118 are sequentially deposited in the opening and the surface of the upper dielectric layer 1110 planarize to yield the intermediate structure shown in FIG. 11C.

Although not shown, it will be understood that as in the embodiments described above the multi-layer charge storing layer 1116 can include a multi-layer charge storing layer including at least one lower or bottom charge-trapping layer closer to the tunnel oxide layer 1114, and an upper or top charge-trapping layer overlying the bottom charge-trapping layer. Generally, the top charge-trapping layer includes a silicon-rich, oxygen-lean nitride layer and includes a majority of a charge traps distributed in multiple charge-trapping layers, while the bottom charge-trapping layer includes an oxygen-rich nitride or silicon oxynitride, and is oxygen-rich relative to the top charge-trapping layer to reduce the number of charge traps therein. In some embodiments, the multi-layer charge storing layer 1116 further includes at least one thin, intermediate or anti-tunneling layer including a dielectric, such as an oxide, separating the top charge-trapping layer from the bottom charge-trapping layer.

Next, a second or channel opening 1120 is anisotropically etched through tunnel oxide layer 1114, multi-layer charge storing layer 1116, and blocking dielectric 1118, FIG. 11D. Referring to FIG. 11E, a semiconducting material 1122 is deposited in the channel opening to form a vertical channel 1124 therein. The vertical channel 1124 can include an annular region in an outer layer of a substantially solid cylinder of semiconducting material, or, as shown in FIG. 11E, can include a separate, layer semiconducting material 1122 surrounding a cylinder of dielectric filler material 1126.

Referring to FIG. 11F, the surface of the upper dielectric layer 1110 is planarized and a layer of semiconducting material 1128 including a second, doped diffusion region 1130, such as a source or a drain, formed therein deposited over the upper dielectric layer to form the device shown.

Referring to FIG. 12, in a gate last scheme a dielectric layer 1202, such as an oxide, is formed over a sacrificial layer 1204 on a surface on a substrate 1206, an opening etched through the dielectric and sacrificial layers and a vertical channel 1208 formed therein. As with embodiments described above, the vertical channel 1208 can include an annular region in an outer layer of a substantially solid cylinder of semiconducting material 1210, such as polycrystalline or mono crystalline silicon, or can include a separate, layer semiconducting material surrounding a cylinder of dielectric filler material (not shown). The dielectric layer 1202 can include any suitable dielectric material, such as a silicon oxide, capable of electrically isolating the subsequently formed gate layer of the memory device 1000 from an overlying electrically active layer or another memory device. The sacrificial layer 1204 can include any suitable material that can be etched or removed with high selectivity relative to the material of the dielectric layer 1202, substrate 1206 and vertical channel 1208.

Referring to FIG. 12B, a second opening 1212 is etched through the etched through the dielectric and sacrificial layers 1202, 1204, to the substrate 1206, and the sacrificial layer 1204 etched or removed. The sacrificial layer 1204 can include any suitable material that can be etched or removed with high selectivity relative to the material of the dielectric layer 1202, substrate 1206 and vertical channel 1208. In one embodiment the sacrificial layer 1204 includes silicon dioxide that can be removed by buffered oxide etch (BOE etch).

Referring to FIGS. 12C and 12D, layers of a tunnel oxide layer 1214, multi-layer charge storing layer 1216, and blocking dielectric 1218 are sequentially deposited in the opening and the surface of the dielectric layer 1202 planarize to yield the intermediate structure shown in FIGS. 12C and 12D. In some embodiments, such as that shown in FIG. 12D, the multi-layer charge storing layer 1216 can be a multi-layer charge storing layer including at least a first or inner charge trapping layer 1216 a closest to the tunnel oxide layer 1214, and a second or outer charge trapping layer 1216 b. Optionally, the first and second charge trapping layers can be separated by an intermediate oxide or anti-tunneling layer 1220.

Next, a gate layer 1222 is deposited into the second opening 1212 and the surface of the upper dielectric layer 1202 planarized to yield the intermediate structure illustrated in FIG. 12E. As with embodiments described above, the gate layer 1222 can include a metal deposited or a doped polysilicon. Finally, an opening 1224 is etched through the gate layer 1222 to form control gate of separate memory devices 1226.

Embodiments of the charge retention devices described herein may be employed in logic circuits to function as machine-memory. Those having skill in the art will appreciate that there are various logic implementations that may embody the described structures, and that the preferred vehicle will vary with the context in which the processes are deployed. For example, if an implementer determines that speed and accuracy are paramount, the implementer may opt for a hardware and/or firmware vehicle; alternatively, if flexibility is paramount, the implementer may opt for a solely software implementation; or, yet again alternatively, the implementer may opt for some combination of hardware, software, and/or firmware. Hence, there are many vehicles that may employ the devices described herein, none of which is inherently superior to the other in that any vehicle to be utilized is a choice dependent upon the context in which the vehicle will be deployed and the specific concerns (e.g., speed, flexibility, or predictability) of the implementer, any of which may vary. Those skilled in the art will recognize that optical aspects of implementations may involve optically-oriented hardware, software, and or firmware.

Although shown and described above as having only two oxynitride layer, i.e., a top and a bottom layer, the present disclosure is not so limited, and the multi-layer charge storing layer can include any number, n, of oxynitride layers, any or all of which may have differing stoichiometric compositions of oxygen, nitrogen and/or silicon. In particular, multi-layer charge storing layers having up to five oxynitride layers each with differing stoichiometric compositions have been produced and tested. However, as will be appreciated by those skilled in the art it is generally desirable to utilize as few layers as possible to accomplish a desired result, reducing the process steps necessary to produce the device, and thereby providing a much simpler and more robust manufacturing process. Moreover, utilizing as few layers as possible also results in higher yields as it is simpler to control the stoichiometric composition and dimensions of the fewer layers.

It will further be appreciated that although shown and described as part of a silicon-oxide-oxynitride-oxide-silicon stack in a memory device, the structure and method of the present disclosure is not so limited, and the silicon-oxide-oxynitride-oxide-silicon structure can be used in or with any semiconductor technology or in any device requiring a charge storing or dielectric layer or stack including, for example, in a split gate flash memory, a TaNOS stack, in a 1T (transistor) SONOS-type cell, a 2T SONOS-type cell, a 3T SONOS-type cell, a localized 2-bit cell, a multilevel programming or cell, and/or a 9T or 12T non-volatile semiconductor memory (NVSM) cells without departing from the scope of the disclosure.

The foregoing detailed description has set forth various embodiments of the devices and/or processes via the use of block diagrams, flowcharts, and/or examples. Insofar as such block diagrams, flowcharts, and/or examples contain one or more functions and/or operations, it will be understood as notorious by those within the art that each function and/or operation within such block diagrams, flowcharts, or examples can be implemented, individually and/or collectively, by a wide range of hardware, software, firmware, or virtually any combination thereof.

Embodiments of the structures described herein may be employed in Application Specific Integrated Circuits (ASICs), Field Programmable Gate Arrays (FPGAs), central processing units (CPUs), digital signal processors (DSPs), or other integrated formats. However, those skilled in the art will recognize that some aspects of the embodiments disclosed herein, in whole or in part, can be equivalently implemented in dedicated memory circuits, for the purpose of storing digital information for data and/or programs running on one or more computers (e.g., as one or more programs running on one or more computer systems), as one or more programs running on one or more processors (e.g., as one or more programs running on one or more microprocessors), as firmware, or as virtually any combination thereof.

In a general sense, those skilled in the art will recognize that the various structures described herein may be embodied, individually and/or collectively, by a wide range of electrical circuitry. As used herein “electrical circuitry” includes, but is not limited to, electrical circuitry having at least one discrete electrical circuit, electrical circuitry having at least one integrated circuit, electrical circuitry having at least one application specific integrated circuit, electrical circuitry forming a general purpose computing device configured by a computer program (e.g., a general purpose computer configured by a computer program which at least partially carries out processes and/or devices described herein, or a microprocessor configured by a computer program which at least partially carries out processes and/or devices described herein), electrical circuitry forming a memory device (e.g., forms of random access memory), and/or electrical circuitry forming a communications device (e.g., a modem, communications switch, or optical-electrical equipment).

Those skilled in the art will recognize that it is common within the art to describe devices and/or processes in the fashion set forth herein, and thereafter use standard engineering practices to integrate such described devices and/or processes into larger systems. That is, at least a portion of the devices and/or processes described herein can be integrated into a network processing system without an undue amount of experimentation. 

What is claimed is:
 1. A memory device comprising: a channel formed from a semiconducting material overlying a surface on a substrate connecting a source and a drain of the memory device; a tunnel oxide layer overlying the channel; and a multi-layer charge storing layer including an oxygen-rich, first oxynitride layer on the tunnel oxide layer in which a stoichiometric composition of the first oxynitride layer results in it being substantially trap free, and an oxygen-lean, second oxynitride layer on the first oxynitride layer in which a stoichiometric composition of the second oxynitride layer results in it being trap dense.
 2. The memory device of claim 1, wherein the channel comprises polysilicon.
 3. The memory device of claim 1, wherein the channel comprises recrystallized polysilicon.
 4. The memory device of claim 1, wherein the channel comprises a silicon nanowire.
 5. The memory device of claim 1, wherein the memory device comprises a non-planar transistor including a gate having multiple surfaces abutting the channel, and wherein the gate comprises the tunnel oxide layer and the multi-layer charge storing layer.
 6. The memory device of claim 5, wherein the gate further comprises a blocking dielectric overlying the multi-layer charge storing layer, and a metal gate layer overlying the blocking dielectric layer
 7. The memory device of claim 6, wherein the blocking dielectric comprises a high K dielectric.
 8. The memory device of claim 1, wherein the second oxynitride layer further comprises a concentration of carbon selected to increase a number of traps therein.
 9. A memory device comprising: an electrically conducting channel formed from a semiconducting material overlying a surface on a substrate connecting a source and a drain of the memory device; and a gate having multiple surfaces abutting the channel, the gate comprising: a tunnel oxide layer overlying the channel; and a multi-layer charge storing layer including a first oxynitride layer closer to the tunnel oxide layer, and a second oxynitride layer, wherein the first oxynitride layer is separated from the second oxynitride layer by an anti-tunneling layer comprising an oxide.
 10. The memory device of claim 9, wherein the channel comprises a silicon nanowire.
 11. The memory device of claim 9, wherein the device comprises a finFET, and wherein the gate further comprises a blocking dielectric overlying the multi-layer charge storing layer, and a metal gate layer overlying the blocking dielectric layer.
 12. The memory device of claim 11, wherein the blocking dielectric comprises a high K dielectric.
 13. The memory device of claim 9, wherein the anti-tunneling layer comprises a portion of the first oxynitride layer that has been oxidized by radical oxidation.
 14. The memory device of claim 9, wherein the first oxynitride layer is a substantially trap free, oxygen-rich, oxynitride layer, and the second oxynitride layer is a trap dense, oxygen-lean, oxynitride layer further comprising a concentration of carbon selected to increase a number of traps therein.
 15. A memory device comprising: a vertical channel formed from a thin projection of semiconducting material extending from a first diffusion region formed on a surface on a substrate to a second diffusion region formed over the surface of the substrate, the vertical channel electrically connecting the first diffusion region to the second diffusion region; a tunnel oxide layer abutting the vertical channel; and a multi-layer charge storing layer abutting the tunnel oxide layer, the multi-layer charge storing layer including a first oxynitride layer comprising an oxygen-rich nitride closer to the tunnel oxide layer, and a second oxynitride layer comprising a silicon-rich, oxygen-lean nitride overlying the first oxynitride layer, wherein the second charge-trapping layer comprises a majority of a charge traps distributed in split charge-trapping region.
 16. The memory device of claim 15, wherein the channel comprises a vertical silicon nanowire.
 17. The memory device of claim 16, wherein the multi-layer charge storing layer further comprises an oxide anti-tunneling layer separating the first oxynitride layer from the second oxynitride layer.
 18. The memory device of claim 16, further comprising a high K blocking dielectric overlying the multi-layer charge storing layer.
 19. The memory device of claim 18, wherein the multi-layer charge storing layer further comprises an oxide anti-tunneling layer separating the first oxynitride layer from the second oxynitride layer.
 20. The structure of claim 15, wherein the second oxynitride layer further comprises a concentration of carbon selected to increase a number of traps therein. 